Şişecam Flat Glass - Sand vs The Other Guys

A glass batch is around 55-70% is silica sand—the main ingredient that gives glass its structure and transparency. The rest is a mix of soda ash, limestone, and other materials like dolomite, alumina, or feldspar, depending on the desired properties. Soda ash lowers the melting point, making it possible to melt sand at workable temperatures. Limestone and the other additives contribute strength, durability, and chemical stability. The batch is often mixed with cullet (recycled glass) which not only reduces waste but also lowers the energy needed to melt the mix. These raw materials are carefully measured, combined, and fed into the furnace where they melt together and flow onto a tin bath to produce float glass. At Şişecam, every piece of glass comes to life through the perfect harmony of nature and technology. ... Cam harmanı yaklaşık %55-70 oranında silis kumundan oluşur. Kum camın yapısını ve şeffaflığını sağlayan ana bileşendir. Harmanın geri kalanı ise soda külü, kireçtaşı ve istenen özelliklere bağlı olarak dolomit, alümina veya feldspat gibi diğer malzemelerin karışımıdır. Soda külü, kumun ergime sıcaklığını düşürerek, onun endüstriyel olarak işlenebilir sıcaklıklarda eritilmesini sağlar. Kireçtaşı ve diğer katkı maddeleri ise dayanım, sağlamlık ve kimyasal kararlılık kazandırır. Harman genellikle cam kırığı (geri dönüştürülmüş cam) ile karıştırılır. Bu sayede yalnızca atıklar azaltılmakla kalmaz, aynı zamanda karışımın ergitilmesi için gereken enerji miktarı da düşürülür. Tüm hammaddeler özenle ölçülür, bir araya getirilir ve fırına verildikten sonra float cam üretimi için kalay banyosu üzerine akıtılır. Şişecam’da her cam, doğa ve teknolojinin mükemmel uyumuyla hayat buluyor. #Şişecam hashtag#FlatGlass hashtag#PoetryoftheFactory